COMPOTEX woven roving fabrics and tapes
COMPOTEX woven roving fabrics and tapes
COMPOTEX woven roving fabrics and tapes
COMPOTEX woven roving fabrics and tapes
COMPOTEX woven roving fabrics and tapes

COMPOTEX woven roving fabrics and tapes

Ask a question Request

  • COMPOTEX woven roving fabrics are plain woven of rovings consisting of non-intertwisted glass fibers. Uniformity in distribution of physical tensions and high physical-chemical performance are achieved owing to positioning of rovings at 90°-angle during weaving process.

  • Physical and mechanical properties

     

    Property Unit

    COMPOTEX

    28563

    COMPOTEX

    29052

    COMPOTEX

    42560

    Mass per unit area g/m² 285±40 290±40 425±40
    Type of weave plain
    Tensile strength
    warp N/2.5cm ≥400 ≥1800 ≥175
    weft N/2.5cm ≥2500 ≥1650 ≥3900
    Thickness mm 0.27±15% 0.28±15% 0.37±15%
    Loss on ignition % ≤1.5 ≤1.5 ≤1.5
    Sizing agent silane
    Standard roll size
    width cm 22(±1.5%) 100(+2/-1%) 25(±1.5%)
    length m ≥50

     

    Property Unit

    COMPOTEX 4

    3014

    COMPOTEX

    60095

    COMPOTEX

    63053

    COMPOTEX

    74013

    Mass per unit area g/m² 430±50 600±60 630±40 740±80
    Type of weave plain
    Tensile strength
    warp Н/2.5cm ≥1764 ≥2500 ≥2750 ≥2940
    weft Н/2.5cm ≥2548 ≥2500 ≥2750 ≥2940
    Thickness mm 0.35±15% 0.58±15% 0.55±15% 0.60±15%
    Loss on ignition % ≤1.5 ≤1.5 ≤1.5 ≤1.5
    Sizing agent silane
    Standard roll size
     width cm

    100(+2%/-1%)

    100(±1.5%)

    100(+2%/-1%)

    100(+2%/-1%)

    length m ≥50

     

    Manufacture of the material with other physical and mechanical properties is accepted upon agreeing about with a consumer.

  • Typical application:

    the fabrics are used as reinforcing elements in manufacture of composite materials and fiber-glass plastics to ensure strength and durability of various structures.

    Composite fiberglass articles made with the use of woven roving fabrics are widely used manufacture of large-sized parts for cars, yachts, powerboats and other small size vessels, aircrafts, especially when during production it is necessary to quickly gain thickness of material at large surface of workpiece.

  • COMPOTEX woven roving fabrics ensure even distribution of bonding and impregnating agents thus making it possible to use the fabrics as reinforcing material in manufacture of composite fiber-glass goods by winding and contact molding.

    The fabrics are made of rovings manufactured in Russia.