  • Glass filled polyamide is a composite material consisting of polyamide reinforced with glass fiber as filler, which ensures high level of mechanical, thermal, and other important performance characteristics of the material.


  • Physical and mechanical properties

     

    Property Unit PA 6-210-DS PA 6-211-DS
    superior grade first grade superior grade first grade

    Ultimate flexural strength

     

    MPa (kgf/cm2)

    ≥250

    (2550)

    ≥200

    (2040)

    ≥260

    (2650)

    ≥245

    (2500)

    Tensile strength MPa (kgf/cm2)

    ≥170

    (1730)

    ≥130

    (1325)

    ≥180

    (1835)

    ≥150

    (1529)

    Impact viscosity, min kJ/m2 (kgf·cm/cm2)

    ≥60

    (61)

    ≥35 (35.7)

    ≥60

    (61)

    ≥44

    (45)

    Specific electrical resistivity
    surface Ohm ≥1014 ≥5х1013 ≥1х1014 ≥1х1013
    volume Ohm·cm ≥1015 ≥5х1013 ≥1х1015 ≥1х1014
    Dielectric strength kV/mm ≥23 ≥20 ≥23 ≥20
    Bending temperature under load °С ≥200 ≥185 ≥200 ≥190
    Mass fraction of filler % 23-33 27-33 30-34 30-34
    Mold shrinkage % 0.45 0.45 0.4-0.6 0.4-0.6

    Manufacture of the material with other physical and mechanical properties is accepted upon agreeing about with a consumer

  • Typical application:

    glass filled polyamides are intended for injection molding or extrusion of engineering-, electrotechnical-, and general-technical purpose articles with increased heat resistance and mechanical behavior.

  • Advantages:

    glass-filled polyamide articles substitute for metals, thermosetting materials or pricier thermoplastics.